山下 享介*; 古賀 紀光*; 川崎 卓郎; 諸岡 聡; 友野 翔平*; 梅澤 修*; Harjo, S.
Materials Science & Engineering A, 819, p.141509_1 - 141509_10, 2021/07
被引用回数:21 パーセンタイル:87.87(Nanoscience & Nanotechnology)In-situ neutron diffraction measurements were performed on a cold-rolled copper-iron (Cu-Fe) alloy during tensile tests at 293 K and 150 K. The roles of Cu and Fe on the deformation behavior of alloys were discussed and clarified. The strength and work-hardening rate of the alloy increased with decreasing test temperature. Furthermore, the phase stress of Fe increased considerably with decreasing test temperature; however, the response of this stress to the applied true stress exhibited no dependence on the temperature. The phase stresses of Cu changed only slightly with decreasing test temperature. However, the Cu phase stress response to the applied true stress increased with decreasing test temperature, indicating an increase in the work-hardening rate. The strengthening of Fe and the increase in the work-hardening of Cu contributed to an increase in the strength and work-hardening rate of the Cu-Fe alloy at low temperatures.
星屋 泰二; 田昭 治*; 安藤 弘栄
日本金属学会誌, 56(7), p.741 - 746, 1992/00
中性子照射したTi-Ni系形状記憶合金の673K以下の温度における高温変形挙動さらには照射後に473,523,573Kで焼鈍した際の変形挙動を引張試験及び硬度試験を用いて調べた。中性子照射によって照射誘起超弾性など特異な変形挙動が生じた。これらは523K以上の温度における照射後焼鈍によって完全に回復した。この原因としては、照射によって生成した空孔などの欠陥移動が熱振動で助長され規則化過程を促進するためである。照射中のTi-Ni系形状記憶合金では、二つの相反する過程が競合して起きる。すなわち、照射誘起不規則と空孔移動によって促進される規則化である。これらの過程は照射温度と照射フルエンスに依存する。